Curing times depend on: the reactivity of the employed
resins , the working-order of the oven
and mass of the material to paint.According to
user requirements this powder polymerizes as follows:
| NORMAL TYPE |
RAPID TYPE |
180
°C=20'
190 °C=15'
200 °C=10' |
160 °C=25'
170 °C=20'
180 °C=10' |
Temperature refers to that object
Specific Weight=1,2 ÷ 1,7
depending on color Glossness 60 °
(ISO 2813)= 90 ÷ 20 gloss
(GlosspðMatt)
Bending on spindle
Dishing ERICHSEN
Direct hit
Reticle adherance
Pencil hardness Wolff-Wilborn
Hardness BUCHHOLZ |
(Uni ISO 1519)=<5
mm
(ISO 1520)=>5 mm
(ISO 6272)=>10 Nm
(Uni ISO 2409)=GT 0
(ASTM D 3363)=H-2H
(ISO 2815)=80-100 |
The a.m data were obtained on laminates previously prepared with crystaline
phospate of zinc salt. |
 
Curing times depend on: the reactivity of the employed
resins , the working-order of the oven
and mass of the material to paint. According to
user requirements this powder polymerizes as follows:
NORMAL
TYPE |
RAPID
TYPE |
180 °C=20'
190 °C=15'
200 °C=10' |
160
°C=25'
170 °C=20'
180 °C=10' |
Temperature refers to that object
Specific Weight = 1,2 ÷ 1,7 depending
on color
Glossness 60°
(ISO 2813)=90÷20 gloss
(GlosspðMatt)
Bending on spindle
Dishing ERICHSEN
Direct hit
Reticle adherance
Pencil hardness Wolff-Wilborn
Hardness BUCHHOLZ |
(Uni ISO 1519)=<5 mm
(ISO 1520)=>5 mm
(ISO 6272)=>10 Nm
(Uni ISO 2409)=GT 0
(ASTM D 3363)=H-2H
(ISO 2815)=80-100 |
The a.m data were obtained on laminates previously prepared with crystaline
phospate of zinc salt. |